Polyesters stabilized with hydrocarbyl trialkoxy silanes



United States Patent 3,488,318 POLYESTERS STABILIZED WITH HYDROCARBYL TRIALKOXY SILANES Mary J. Stewart, Riddlewood, Media, and Otto K.

Carlson, Marcus Hook, Pa., assignors to FMC Corporation, Philadelphia, Pa., a corporation of Delaware N0 Drawing. Filed Mar. 25, 1968, Ser. No. 715,588 Int. Cl. C08g 51/58 U.S. Cl. 26045.7 Claims ABSTRACT OF THE DISCLOSURE A thermal stabilized polyester composition comprising a highly polymeric linear polyester and a thermal stabilizer selected from those represented by the formula wherein R R and R are lower alkyl radicals having from 1 to 6 carbon atoms and R is a radical selected from the group consisting of lower alkyl containing from 1 to 6 carbon atoms, lower alkenyl containing from 2 to 6 carbon atoms, and phenyl.

This invention relates to highly polymeric linear polyester resins that possess improved thermal stability and to a method of producing same.

The fiber and film-forming linear polyester resins used in the present invention can be prepared by first carrying out a condensation reaction between a suitable aromatic dicarboxylic acid or ester thereof which does not contain any ethylenic unsaturation and a diol to form a prepolymer. The resulting prepolymer is then polycondensed to form the desired polyester resin. When an ester of a dicarboxylic acid is used as the starting material, it is first reacted with a diol in the presence of a transesterification or ester-interchange catalyst by means of an ester-interchange reaction; whereas when a dicarboxylic acid is used as the starting material, it is first subjected to a direct esterification reaction with a diol in the presence of what is generally called a first stage additive or ether inhibitor. In either instance, the resulting reaction product, which may be generally described as a polyester prepolymer, is then polycondensed in the presence of a polycondensation catalyst to form a polyester resin.

For example, in the case of the transesterification method of preparing polyethylene terephthalate, ethylene glycol is reacted with dimethyl terep hthalate to form a polyester prepolymer which is comprised mainly of his- Z-hydroxyethyl terephthalate; or in the direct esterification method, ethylene glycol is reacted with terephthalic acid to form the resulting polyester prepolymer which is then polycondensed to form the desired polyester resin.

Linear polyester resins, such as polyethylene terephthalate and others, are widely used in the production of films and fibers and the like. However, it is generally known that such polyester products degrade when exposed to heat for a substantial period of time. Such deg radation is particularly a problem in the extrusion and spinning processes of the finished resins to form the above-denoted products. Additionally, the fibers produced from such resins are extensively used in the textile field and, as a result of this application, are subjected to rather extreme temperatures in the processes of washing, drying, and ironing. Therefore, it is highly desirable that the polyester resin composition possess as much stability at high temperatures as possible.

3,488,318 Patented Jan. 6, 1970 ice Therefore, it is an object of the present invention to prepare a highly polymeric linear polyester resin composition which exhibits improved thermal stability.

Another object of the present invention is to provide a method of preparing linear polyester resin exhibiting such a high degree of thermal stability.

These and other objects are accomplished in accordance with the present invention with a stabilized polyester composition comprising a highly polymeric linear polyester containing a stabilizing amount of a thermal stabilizer selected from those represented by the formula 0R3 RzOS iR4 R1 wherein R R and R are lower alkyl radicals having from .1 to 6 carbon atoms and R is a radical selected from the group consisting of lower alkyl containing from 1 to 6 carbon atoms, lower alkenyl containing from 2 to 6 carbon atoms, and phenyl' Among the silane compounds which can be used as thermal stabilizers in the present compositions are, for example, propyltriethoxysilane, allyltriethoxysilane, hexyldimethoxyethoxysilane, methyltrimethoxysilane, butyltributoxysilane, phenyltrimethoxysilane, phenyltripropoxysilane, 1-buteny1trimethoxysilane, and 2-pentenyltributoxysilane.

The highly polymeric linear polyester resins used in the preparation of the subject thermal stabilized polyester compositions can be prepared via either the conventional ester-interchange reaction or direct esterfication method, both of which are thoroughly disclosed throughout the prior art.

In the practice of the present invention, it has been found that it is preferred to mix or blend the present thermal stabilizers in the polyester resin immediately after the polycondensation step has been completed, at atmospheric pressure, while the resin is still molten.

It has been found that the present thermal stabilizers, as defined above, are effective as such in polyester resin compositions when employed in amounts ranging from about 0.01% to about 0.5%, by weight, based on the weight of the linear polyester resin. Usually, it has been found that concentrations ranging from about 0.02% to about 0.3%, by Weight, are preferred in most instances. However, when indicated, concentrations less or greater than the above can be used, but their effectiveness is generally reduced proportionally.

The following examples will further serve to illustrate the present invention, although it will be understood that these examples are included merely for the purpose of illustration and are not intended to limit the scope f the present invention. All parts are by weight, u less otherwise indicated.

EXAMPLE I A blended mixture comprising 474 g. of terephthalic acid, 288 mls. of ethylene glycol and 149 mls. of triethylamine was charged into a reaction vessel equipped with a nitrogen inlet, a Dean-Starke separating apparatus, heating means and stirring means. The reaction mixture was agitated and the temperature was raised to about 197 C. under a nitrogen blanket at atmospheric pressure. At about C., a water-triethylamine azeotropic mixture started to distill off. The azeotropic mixture was continuously separated by means of the Dean-Starke apparatus, and the triethylamine recovered was continuously returned to the reaction vessel. The reaction mixture became almost clear. Then, the temperature was allowed to rise to about 230 C. over a one-hour period to remove all the triethylamine and any excess glycol. The prepolymer product was allowed to cool under an atmosphere of nitrogen.

EXAMPLE II Fifty grams of the prepolymer product of Example I was mixed with 0.02 g. of antimony sec-butoxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 2 hours to bring about the polycondensation of the polyester prepolymer and formation of a polyester resin. The polyethylene terephthalate resin formed had an original intrinsic viscosity of 0.88, a degraded intrinsic viscosity of 0.69, and the percentage broken bonds was calculated as 0.132.

EXAMPLE III Fifty grams of the prepolymer product of Example I was mixed with 0.02 g. of antimony sec-butoxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 2 hours to bring about the polycondensation of the prepolymer and formation of a polyester resin. After the polycondensation reaction had been completed, 0.02 ml. of allyltriethoxysilane was thoroughly stirred into the polyester resin while still molten at atmospheric pressure, after which the resin product was cooled. The resulting polyethylene terephthalate composition had an original intrinsic viscosity of 0.67, a degraded intrinsic viscosity of 0.61, and the percentage broken bonds value was calculated as 0.066.

EXAMPLE IV Fifty grams of the prepolymer product of Example I was mixed with 0.02 g. of antimony sec-butoxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 2 hours to bring about the polycondensation of the prepolymer and formation of a polyester resin. After the polycondensation reaction had been completed, 0.02 ml. of methyltrimethoxysilane was thoroughly stirred into the polyester resin while still molten at atmospheric pressure, after which the resin product was cooled. The resulting polyethylene terephthalate composition had an original intrinsic viscosity of 0.66, a degraded intrinsic viscosity of 0.62, and the percentage broken bonds was calculated as 0.038.

EXAMPLE V Fifty grams of the prepolymer product of Example I was mixed with 0.02 g. of antimony sec-butoxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 2 hours to bring about the polycondensation of the prepolymer and formation of a polyester resin. After the polycondensation reaction had been completed, 0.02 ml. of phenyltrimethoxysilane was thoroughly stirred into the polyester resin while still molten at atmospheric pressure, after which the resin product was cooled. The resulting polyethylene terephthalate composition had an original intrinsic viscosity of 0.65, a degraded intrinsic viscosity of 0.56, and the percentage broken bonds value was calculated as 0.109.

EXAMPLE VI A mixture comprising 600 g. of dimethyl terephthalate, 396 mls. of ethylene glycol and 0.24 g. of lithium hydride was charged into a reaction vessel equipped with a nitrogen inlet, heating means and stirring means. The reaction mixture was agitated and heated at atmospheric pressure at 198 C. under a nitrogen blanket. The reaction mixture was held at about 198 C. for about two hours, during which time by-product methyl alcohol was distilled off. Then, the temperature of the reaction mixture was allowed to rise to 230 C. over a period of about one hour to distill off any remaining by-product methyl alcohol and ethylene glycol and form a polyester prepolymer. The prepolymer product was allowed to cool under an atmosphere of nitrogen.

EXAMPLE VII Fifty grams of the prepolymer product of ExampleVI was mixed with 0.02 g. of antimony trioxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 3 hours to bring about the polycondensation of the polyester prepolymer and formation of a polyester resin. The polyester resin formed had an original intrinsic viscosity of 1.13, a degraded intrinsic viscosity of 0.76, and the percentage broken bonds was calculated as 0.169.

EXAMPLE VIII Fifty grams of the prepolymer product of Example VI was mixed with 0.02 g. of antimony trioxide and placed in a reaction vessel. The reaction mixture was heated at about 280 C. under reduced pressure of from about 0.05 to about 0.1 mm. of mercury while under agitation for about 3 hours to bring about condensation of the polyester prepolymer and formation of a polyester resin. After the polycondensation reaction had been completed, 0.02 ml. of phenyltrimethoxysilane was thoroughly stirred into the polyester resin while still molten at atmospheric pressure, after which the resin product was cooled. The resultant polyester resin composition had an original intrinsic viscosity of 0.96, a degraded intrinsic viscosity of 0.75, and the percentage broken bonds value was calculated as 0.119.

In the above examples, the original intrinsic viscosity values of the polyester resin products were obtained by measuring the intrinsic viscosities of the resin compositions as produced.

The degraded intrinsic viscosity values were determined by the following procedure: The polyester resin composition was ground and passed through a 10 U.S.S. mesh screen and dried at C. in the vacuo for 16 hours, then cooled in a desiccator. Two to three grams of this dried resin was then placed in a test tube which was then inserted into an aluminum block preheated to 280 C. (:L0.5 C.). The block was then sealed and evacuated to 0.1 mm. of mercury. After holding for about 10-15 seconds, the block was filled with dried, oxygenfree nitrogen gas. This vacuum-nitrogen purge was then repeated for a total of three times; the entire process took 5-7 minutes. Then, the resin sample was left in the heated block for an additional two hours under a slow stream of nitrogen. After this two-hour period, the resin sample was removed from the block and placed in a desiccator which was first evacuated and then filled with nitrogen. The intrinsic viscosity of the resin product was then determined and such an intrinsic viscosity value is noted in the examples above as the degraded intrinsic viscosity.

The percentage broken bonds values indicated in the above examples were calculated by the use of the following equation:

K Ill K l/a Percent Broken Bonds=[() 9.6 10

The value of K and a may be found in the literature, such as Conix, A., Makromol, Chemie 26, p. 226 (1958), wherein K=0.00021 and a=0.82. V; in the above formula is the degraded or final intrinsic viscosity value, and V, is the original or initial intrinsic viscosity value.

All of the intrinsic viscosity determinations of the polyester resin products produced in the above examples were determined in a 60% phenol-40% tetrachloroethane solution, wt./wt., at 30 C., according to conventional laboratory procedure.

The results in the above examples indicate that the present additives, when added to linear polyester resins, act to stabilize or reduce the degradation eflfects of higher temperatures upon such polyester resins. The change in intrinsic viscosity or the difference between the original intrinsic viscosity and the degraded intrinsic viscosity is a direct measure of the heat stabilizing effect that the present thermal stabilizers have upon polyester resins and can be readily calculated from the above results.

When the controls above, Examples II and VII, are compared with the corresponding examples wherein the same catalyst systems and starting materials were used, but with the addition of a thermal stabilizer of the present invention, it can readily be seen from the intrinsic viscosity values and the percentage broken bonds values that the present stabilizers act to limit the amount of degradation that takes place when polyester resin products are exposed to elevated temperatures for prolonged periods of time.

The present invention has been illustrated with particular respect to the stabilization of polyethylene terephthalate. However, the present thermal stabilizers are also effective in stabilizing any fibers and film-forming linear polyesters and copolyesters; for example, those derived from aromatic dicarboxylic acids, such as isophthalic acid, and 4,4-diphenyldicarboxylic acid, or ester derivatives thereof, and suitable diols, such as glycols of the series HO(CH ),,OH, where n is 2 to 10.

It will be apparent that various different embodiments can be made practicing this invention without departing from the spirit and scope thereof, and therefore, it is not intended to be limited, except as indicated in the appended claims.

We claim:

1. A stabilized polyester composition comprising a linear saturated polyester containing a stabilizing amount of a compound selected from those represented by the formula RzOSiR4 wherein R R and R are lower alkyl radicals and R is a radical selected from the group consisting of lower alkyl, lower alkenyl, and phenyl.

2. The composition of claim 1 wherein the polyester is polyethylene terephthalate.

3. The composition of claim 1 containing from about 0.01% to about 0.5%, by weight, of a thermal stabilizer, based on the weight of the linear polyester.

4. The composition of claim 1 wherein the compound is methyltrimethoxysilane.

5. The composition of claim 1 wherein the compound is allyltriethoxysilane.

6. The composition of claim 1 wherein the compound is phenyltrimethoxysilane.

7. The composition of claim 1 wherein the compound is propyltriethoxysilane.

8. The composition of claim 1 wherein the compound is phenyltripropoxysilane.

9. The composition of claim 1 wherein the compound is hexyldimethoxyethoxysilane.

10. The composition of claim 1 wherein the compound is 2-pentenyltributoxysilane.

References Cited UNITED STATES PATENTS 2,789,100 4/1957 Wilson 260-31.8 3,174,945 3/1965 Taylor et al. 260- 3,346,542 10/1967 Koepp et al. 260- DONALD E. CZAJA, Primary Examiner R. A. WHITE, Assistant Examiner 